Grease, Cartridge, > 220 °C, 60 strokes, 10-1 mm: 265-295: 100000 strokes, 10-1 mm: - 20 to + 50 (325 max.), 72 hours at 100 °C, 10-1 mm: - 20 to + 50 change, 2 max. at 150 °C, EAN code: 7316571182285
Brand | SKF |
---|---|
Mfr Part No. | LGHB 2/0.4 |
Acorn Code | LGHB2/0.4-SKF |
HS Code | 2710 12 15 00 |
COO | Netherlands (NL) |
SKF LGHB 2 is a high viscosity, mineral oil based grease, using calcium sulphonate complex thickener. Formulated to withstand high temperatures and extreme loads, it is suitable for a wide range of applications, especially in the cement, mining and metals segments.
Features & benefits:
• Excellent load capacity, anti-oxidation and corrosion protection even with large water ingress
• Withstands peak temperatures of 200 °C (390 °F)
Typical applications:
• Steel on steel plain bearings
• Pulp and paper making machines
• Asphalt vibrating screens
• Continuous casting machines
• Sealed spherical roller bearings operating up to 150 °C (300 °F)
• Work roll bearings in steel industry
• Mast rollers of fork lift trucks
Manufacturer Product Code | LGHB 2/0.4 |
---|---|
Basic Product Description | High visc. high temp. grease, cartridge |
Size (Per Unit) | 420 ml |
UOM | Each |
Base Oil Viscosity cSt @ 40°C | 400 |
Weight (Kg) | 0.4 |
Dropping point | > 220 °C |
Penetration DIN ISO 2137 | 60 strokes, 10-1 mm: 265-295: 100000 strokes, 10-1 mm: - 20 to + 50 (325 max.) |
Roll stability ASTM D1831 | 72 hours at 100 °C, 10-1 mm: - 20 to + 50 change |
Corrosion protection ISO 11007 | Standard (distilled water): 0-0; Water wash out: 0-0; Salt water test (100% salt water): 0-0 |
Oil separation DIN 51 817 | 7 days at 60 °C: 1-3 % |
Copper corrosion DIN 51811 | 2 max. at 150 °C |
Rolling bearing grease life | ROF test, L50 life at 10000 r/min: > 1000 hrs at 130 °C |
EP performances DIN 51350 | Wear scar DIN 51350/5,1400N: 0.86 mm; 4-ball test, welding load DIN 51350/4: > 4000 N |
Thickener | Complex calcium sulphonate |
Base type | Mineral |
Colour | Brown |
Container | Cartridge |
Water resistence | 3 hours at 90 °C: 1 max. |
Operating Time | -20°C |
Ex-2 Features 2 | 60 strokes, 10-1 mm: 265-295: 100000 strokes, 10-1 mm: - 20 to + 50 (325 max.) |
Ex-3 Features 3 | 72 hours at 100 °C, 10-1 mm: - 20 to + 50 change |
Ex-4 Features 4 | Standard (distilled water): 0-0; Water wash out: 0-0; Salt water test (100% salt water): 0-0 |
Series | 7 days at 60 °C: 1-3 % |
Model | 2 max. at 150 °C |
In-3 Internal Features 3 | ROF test, L50 life at 10000 r/min: > 1000 hrs at 130 °C |
In-6 Internal Features 6 | Wear scar DIN 51350/5,1400N: 0.86 mm; 4-ball test, welding load DIN 51350/4: > 4000 N |
Te-2 Laser Line Length | 3 hours at 90 °C: 1 max. |
Lower Operating Temperature | -20°C |
Upper Operating Temperature | +150°C |
Basic Reference | Grease |
EAN code | 7316571182285 |